Nanoimprint lithography (NIL) is a method of fabricating nanometer scale patterns. It is a simple nanolithography process with low cost, high throughput and high resolution. It creates patterns by mechanical deformation of imprint resist and subsequent processes. The imprint resist is typically a monomer or polymer formulation that is cured by heat or UV light during the imprinting. Adhesion between the resist and the template is controlled to allow proper release.
- 1 History
- 2 Processes
- 3 Schemes
- 4 Applications
- 5 Benefits
- 6 Concerns
- 7 Removal of residual layers
- 8 Proximity effects
- 9 3D-patterning
- 10 Alternative approaches
- 11 The future of nanoimprint
- 12 References
- 13 External links
The term "nanoimprint lithography" was coined in the scientific literature in 1996, when Prof. Stephen Chou and his students published a report in Science, although hot embossing (now taken as a synonym of NIL) of thermoplastics had been appearing in the patent literature for a few years already. Soon after the Science paper, many researchers developed different variations and implementations. At this point, nanoimprint lithography has been added to the International Technology Roadmap for Semiconductors (ITRS) for the 32 and 22 nm nodes.
There are many different types of nanoimprint lithography, but three of them are most important: thermoplastic nanoimprint lithography, photo nanoimprint lithography and resist-free direct thermal nanoimprint lithography.
Thermoplastic nanoimprint lithography
Thermoplastic nanoimprint lithography (T-NIL) is the earliest nanoimprint lithography developed by Prof. Stephen Chou's group. In a standard T-NIL process, a thin layer of imprint resist (thermoplastic polymer) is spin coated onto the sample substrate. Then the mold, which has predefined topological patterns, is brought into contact with the sample and they are pressed together under certain pressure. When heated up above the glass transition temperature of the polymer, the pattern on the mold is pressed into the softened polymer film. After being cooled down, the mold is separated from the sample and the pattern resist is left on the substrate. A pattern transfer process (reactive ion etching, normally) can be used to transfer the pattern in the resist to the underneath substrate.
Alternatively, cold welding between two metal surfaces could also transfer low-dimensional nanostructured metal without heating (especially for critical sizes less than ~10 nm),. Three-dimensional structures can be fabricated by repeating this procedure. The cold welding approach has the advantage of reducing surface contact contamination or defect due to no heating process, which is a main problem in the latest development and fabrication of organic electronic devices as well as novel solar cells.
Photo nanoimprint lithography
In photo nanoimprint lithography (P-NIL), a photo (UV) curable liquid resist is applied to the sample substrate and the mold is normally made of transparent material like fused silica or PDMS. After the mold and the substrate are pressed together, the resist is cured in UV light and becomes solid. After mold separation, a similar pattern transfer process can be used to transfer the pattern in resist onto the underneath material. The use of a UV-transparent mold is difficult in a vacuum, because a vacuum chuck to hold the mold would not be possible.
Resist-free direct thermal nanoimprint lithography
Different from the above mentioned nanoimprint methods, resist-free direct thermal nanoimprint does not require an extra etching step to transfer patterns from imprint resists to the device layer.
In a typical process, photoresist patterns are first defined using photolithography. A polydimethylsiloxane (PDMS) elastomer stamp is subsequently replica molded from the resist patterns. Further, a single-step nanoimprint directly molds thin film materials into desired device geometries under pressure at elevated temperatures. The imprinted materials should have suitable softening characteristics in order to fill up the pattern. Amorphous semiconductors (for example chalcogenide glass) demonstrating high refractive index and wide transparent window are ideal materials for the imprint of optical/photonic device.
This direct imprint patterning approach offers a monolithic integration alternative with potentially improved throughput and yield, and may also enable roll-to-roll processing of devices over large substrate areas inaccessible using conventional lithographic patterning methods.
Full wafer nanoimprint
In a full wafer nanoimprint scheme, all the patterns are contained in a single nanoimprint field and will be transferred in a single imprint step. This allows a high throughput and uniformity. An at least 8-inch (203 mm) diameter full-wafer nanoimprint with high fidelity is possible.
To ensure the pressure and pattern uniformities of full wafer nanoimprint processes and prolong the mold lifetime, a pressing method utilizing isotropic fluid pressure, named Air Cushion Press (ACP) by its inventors, is developed and being used by commercial nanoimprint systems. Alternatively, roll on technologies (e.g. roll to plate) in combination with flexible stampers (e.g. PDMS) have been demonstrated for full wafer imprint.
Step and repeat nanoimprint
Nanoimprint can be performed in a way similar to the step and repeat optical lithography. The imprint field (die) is typically much smaller than the full wafer nanoimprint field. The die is repeatedly imprinted to the substrate with certain step size. This scheme is good for nanoimprint mold creation.
Nanoimprint lithography has been used to fabricate devices for electrical, optical, photonic and biological applications. For electronics devices, NIL has been used to fabricate MOSFET, O-TFT, single electron memory. For optics and photonics, intensive study has been conducted in fabrication of subwavelength resonant grating filter, surface-enhanced Raman spectroscopy(SERS) sensor, polarizers, waveplate, anti-reflective structures, integrated photonics circuit and plasmonic devices by NIL. In the context of opto-electronic devices such as LEDs and solar cells, NIL is being investigated for out- and incoupling structures. Sub-10 nm nanofluidic channels had been fabricated using NIL and used in DNA stretching experiment. Currently, NIL is used to shrink the size of biomolecular sorting device an order of magnitude smaller and more efficient.
A key benefit of nanoimprint lithography is its sheer simplicity. The single greatest cost associated with chip fabrication is the optical lithography tool used to print the circuit patterns. Optical lithography requires high powered excimer lasers and immense stacks of precision ground lens elements to achieve nanometer scale resolution. There is no need for complex optics or high-energy radiation sources with a nanoimprint tool. There is no need for finely tailored photoresists designed for both resolution and sensitivity at a given wavelength. The simplified requirements of the technology lead to its low cost.
Silicon master molds can be used up to a few thousands imprints while nickel molds can last for up to a ten of thousand cycles
Imprint lithography is inherently a three-dimensional patterning process. Imprint molds can be fabricated with multiple layers of topography stacked vertically. Resulting imprints replicate both layers with a single imprint step, which allows chip manufactures to reduce chip fabrication costs and improve product throughput. As mentioned above, the imprint material does not need to be finely tuned for high resolution and sensitivity. A broader range of materials with varying properties are available for use with imprint lithography. The increased material variability gives chemists the freedom to design new functional materials rather than sacrificial etch resistant polymers. A functional material may be imprinted directly to form a layer in a chip with no need for pattern transfer into underlying materials. The successful implementation of a functional imprint material would result in significant cost reductions and increased throughput by eliminating many difficult chip fabrication processing steps.
The key concerns for nanoimprint lithography are overlay, defects, template patterning and template wear. However, recently Kumar et al. have shown that amorphous metals (metallic glasses) can be patterned on sub-100 nm scale, which can significantly reduce the template cost.
As with immersion lithography, defect control is expected to improve as the technology matures. Defects from the template with size below the post-imprint process bias can be eliminated. Other defects would require effective template cleaning and/or the use of intermediate polymer stamps. When vacuum is not used during the imprint process, air can get trapped, resulting in bubble defects. This is because the imprint resist layer and the template or stamp features are not perfectly flat. There is an elevated risk when the intermediate or master stamp contains depressions (which are especially easy air traps), or when the imprint resist is dispensed as droplets just before imprinting, rather than pre-spun onto the substrate. Sufficient time must be allowed for the air to escape. These effects are much less critical if flexible stamper materials are used, e.g. PDMS. Another issue is adhesion between stamp and resist. High adhesion (sticking) may delaminate resist, which then stays on stamp. This effect degrades pattern, reduces yield and damages stamp. It can be mitigated by employing an FDTS antistiction layer on a stamp.
High resolution template patterning can currently be performed by electron beam lithography or focused ion beam patterning; however at the smallest resolution, the throughput is very slow. As a result, optical patterning tools will be more helpful if they have sufficient resolution. Such an approach has been successfully demonstrated by Greener et al. whereby robust templates were rapidly fabricated by optical patterning of a photoresist-coated metal substrate through a photomask. If homogeneous patterns on large areas are required, interference lithography is a very attractive patterning technique. Other patterning techniques (including even double patterning) may also be used. Kumar and Schroers at Yale developed the nanopatterning of amorphous metals which can be used as inexpensive templates for nanoimprinting. Currently, state-of-the-art nanoimprint lithography can be used for patterns down to 20 nm and below.
The use of substantial pressure to not only contact but also penetrate a layer during imprinting accelerates the wear of imprint templates compared to other types of lithographic masks. Template wear is reduced with proper use of an anti-adhesion FDTS monolayer coating on a stamp. A very efficient and precise AFM based method for characterizing the degradation of PDMS stamps enables to optimize materials and processes in order to minimize wear.
Future applications of nanoimprint lithography may involve the use of porous low-κ materials. These materials are not stiff and, as part of the substrate, are readily damaged mechanically by the pressure of the imprint process.
Removal of residual layers
A key characteristic of nanoimprint lithography (except for electrochemical nanoimprinting) is the residual layer following the imprint process. It is preferable to have thick enough residual layers to support alignment and throughput and low defects. However, this renders the nanoimprint lithography step less critical for critical dimension (CD) control than the etch step used to remove the residual layer. Hence, it is important to consider the residual layer removal an integrated part of the overall nanoimprint patterning process. In a sense, the residual layer etch is similar to the develop process in conventional lithography. It has been proposed to combine photolithography and nanoimprint lithography techniques in one step in order to eliminate the residual layer.
Nanoimprint lithography relies on displacing polymer. This could lead to systematic effects over long distances. For example, a large, dense array of protrusions will displace significantly more polymer than an isolated protrusion. Depending on the distance of this isolated protrusion from the array, the isolated feature may not imprint correctly due to polymer displacement and thickening. Resist holes can form in between groups of protrusions. Likewise, wider depressions in the template do not fill up with as much polymer as narrower depressions, resulting in misshapen wide lines. In addition, a depression at the edge of a large array fills up much earlier than one located in the center of the array, resulting in within-array uniformity issues.
A unique benefit of nanoimprint lithography is the ability to pattern 3D structures, such as damascene interconnects and T-gates, in fewer steps than required for conventional lithography. This is achieved by building the T-shape into the protrusion on the template. Similarly, nanoimprint lithography can be used to replicate 3D structures created using Focused Ion Beam. Although the area that can be patterned using Focused Ion Beam is limited, it can be used, for example to imprint structures on the edge of optical fibers.
Electrochemical nanoimprinting can be achieved using a stamp made from a superionic conductor such as silver sulfide. When the stamp is contacted with metal, electrochemical etching can be carried out with an applied voltage. The electrochemical reaction generates metal ions which move from the original film into the stamp. Eventually all the metal is removed and the complementary stamp pattern is transferred to the remaining metal.
Laser assisted direct imprint
Laser assisted direct imprint (LADI) is a rapid technique for patterning nanostructures in solid substrates and it does not require etching. A single or multiple excimer laser pulses melt a thin surface layer of substrate material, and a mold is embossed into the resulting liquid layer. A variety of structures with resolution better than 10 nm have been imprinted into silicon using LADI, and the embossing time is less than 250 ns. The high resolution and speed of LADI, attributed to molten silicon’s low viscosity (one-third that of water), could open up a variety of applications and be extended to other materials and processing techniques.
Ultrafast Nanoimprint Lithography or Pulsed-NIL is a technique based on the use of stamps with an heating layer integrated beneath the nanopatterned surface. Injecting a single, short (<100 μs), intense current pulse into the heating layer causes the surface temperature of the stamp to raise suddenly by several hundreds degrees °C. This results in the melting of the thermoplastic resist film pressed against it and the swift indentation of the nanostructures. In addition to the high throughput, this fast process has other advantages, namely, the fact that it can be straightforwardly scaled up to large surfaces, and reduces the energy spent in the thermal cycle with respect to the standard thermal NIL. This approach is currently pursued by ThunderNIL srl.
Roller processes are very well suited for large substrates (full wafer), and large scale production since they can be implemented into production lines. If used with a soft stamper, the process (imprint as well as demoulding) can be extremely soft and tolerant to surface roughness or defects. So the processing even of extremely thin and brittle substrates is possible. Imprints of silicon wafers down to a thickness of 50 µm have been demonstrated using this process. For UV-Roller-NIL on opaque substrates, the UV light must flash through the flexible stamper, e.g. by integrating UV-LEDs into a quartz glass drum.
The future of nanoimprint
Nanoimprint lithography is a simple pattern transfer process that is neither limited by diffraction nor scattering effects nor secondary electrons, and does not require any sophisticated radiation chemistry. It is also a potentially simple and inexpensive technique. However, a lingering barrier to nanometer-scale patterning is the current reliance on other lithography techniques to generate the template. It is possible that self-assembled structures will provide the ultimate solution for templates of periodic patterns at scales of 10 nm and less. It is also possible to resolve the template generation issue by using a programmable template in a scheme based on double patterning.
As of October 2007, Toshiba is the only company to have validated nanoimprint lithography for 22 nm and beyond. What is more significant is that nanoimprint lithography is the first sub-30 nm lithography to be validated by an industrial user.
- Chou, S.Y.; Krauss, P.R.; Renstrom, P.J. (1996). "Imprint Lithography with 25-Nanometer Resolution". Science. 272 (5258): 85–7. Bibcode:1996Sci...272...85C. doi:10.1126/science.272.5258.85.
- Whitesides George M.; et al. (2005). "New Approaches to Nanofabrication: Molding, Printing, and Other Techniques". Chem. Rev. 105 (4): 1171–1196. doi:10.1021/cr030076o. PMID 15826012.
- Yang Lu et al., "Cold Welding of Ultrathin Gold Nanowires," Nature Nanotechnology, 5, Feb.14 2010, p. 213-224. doi:10.1038/nnano.2010.4
- C. M. Sotomayor Torres et al., "Nanoimprint lithography: an alternative nanofabrication approach," Materials Science and Engineering: C, Volume 23, Issues 1-2, 15 January 2003, Pages 23-31 .
- Zou Y.; et al. (2014). "High-Performance, High-Index-Contrast Chalcogenide Glass Photonics on Silicon and Unconventional Non-planar Substrates". Advanced Optical Materials. 2 (5): 478–486. arXiv:1308.2749. doi:10.1002/adom.201300489.
- Han T.; et al. (2010). "Low loss Chalcogenide glass waveguides by thermal nano-imprint lithography". Optics Express. 18 (18): 19286–19291. Bibcode:2010OExpr..1819286H. doi:10.1364/oe.18.019286. PMID 20940824.
- Zou Y.; et al. (2014). "Solution Processing and Resist-Free Nanoimprint Fabrication of Thin Film Chalcogenide Glass Devices: Inorganic-Organic Hybrid Photonic Integration". Advanced Optical Materials. 2 (8): 759–764. doi:10.1002/adom.201400068.
- Gao H, Tan H, Zhang W, Morton K, Chou SY (November 2006). "Air cushion press for excellent uniformity, high yield, and fast nanoimprint across a 100 mm field". Nano Lett. 6 (11): 2438–41. Bibcode:2006NanoL...6.2438G. doi:10.1021/nl0615118. PMID 17090070.
- Hauser, Hubert; Tucher, Nico; Tokai, Katharina; Schneider, Patrick; Wellens, Christine; Volk, Anne; Seitz, Sonja; Benick, Jan; Barke, Simon (2015-01-01). "Development of nanoimprint processes for photovoltaic applications" (PDF). Journal of Micro/Nanolithography, MEMS, and MOEMS. 14 (3): 031210. Bibcode:2015JMM&M..14c1210H. doi:10.1117/1.JMM.14.3.031210. ISSN 1932-5150.
- Xu, Zhida; Wu, Hsin-Yu; Ali, Usman; Jiang, Jing; Cunningham, Brian; Liu, Logan (2011). "Nanoreplicated positive and inverted sub-micron polymer pyramids array for surface enhanced Raman spectroscopy (SERS)". Journal of Nanophotonics. 5 (1): 053526. arXiv:1402.1733. Bibcode:2011JNano...5R3526X. doi:10.1117/1.3663259.
- Hao, Jianjun; Palmieri, Frank; Stewart, Michael D.; Nishimura, Yukio; Chao, Huang-Lin; Collins, Austin; Willson, C. Grant. Octa(hydridotetramethyldisiloxanyl) silsesquioxane as a synthetic template for patternable dielectric materials. Polymer Preprints (American Chemical Society, Division of Polymer Chemistry) (2006), 47(2), 1158-1159.
- Palmieri, Frank; Stewart, Michael D.; Wetzel, Jeff; Hao, Jianjun; Nishimura, Yukio; Jen, Kane; Flannery, Colm; Li, Bin; Chao, Huang-Lin; Young, Soo; Kim, Woon C.; Ho, Paul S.; Willson, C. G. Multi-level step and flash imprint lithography for direct patterning of dielectrics. Proceedings of SPIE-The International Society for Optical Engineering (2006), 6151
- Golden Kumar; Hong Tang & Jan Schroers (Feb 2009). "Nanomoulding with amorphous metals". Nature. 457 (7231): 868–72. Bibcode:2009Natur.457..868K. doi:10.1038/nature07718. PMID 19212407.
- "Imprio 250 Nano-Imprint Lithography Systems". Retrieved 2008-04-24.
- H. Hiroshima and M. Komuro, Jpn. J. Appl. Phys. 46, pp. 6391-6394 (2007).
- X. Liang et al., Nanotechnology 18, 025303 (2007).
- Jesse Greener, Wei Li, Judy Ren, Dan Voicu, Viktoriya Pakharenko, Tian Tang and Eugenia Kumacheva "Rapid, cost-efficient fabrication of microfluidic reactors in thermoplastic polymers by combining photolithography and hot embossing" Lab Chip, 2010, doi:10.1039/b918834g.
- Wolf, Andreas J.; Hauser, Hubert; Kübler, Volker; Walk, Christian; Höhn, Oliver; Bläsi, Benedikt (2012-10-01). "Origination of nano- and microstructures on large areas by interference lithography". Microelectronic Engineering. Special issue MNE 2011 - Part II. 98: 293–296. doi:10.1016/j.mee.2012.05.018.
- Bläsi, B.; Tucher, N.; Höhn, O.; Kübler, V.; Kroyer, T.; Wellens, Ch.; Hauser, H. (2016-01-01). "Large area patterning using interference and nanoimprint lithography". Micro-Optics 2016. 9888. pp. 98880H–98880H–9. doi:10.1117/12.2228458.
- Yasuaki Ootera; Katsuya Sugawara; Masahiro Kanamaru; Ryousuke Yamamoto; Yoshiaki Kawamonzen; Naoko Kihara; Yoshiyuki Kamata; Akira Kikitsu (2013). "Nanoimprint Lithography of 20-nm-Pitch Dot Array Pattern Using Tone Reversal Process". Japanese Journal of Applied Physics. 52 (10R): 105201. Bibcode:2013JaJAP..52j5201O. doi:10.7567/JJAP.52.105201.
- Tucher, Nico; Höhn, Oliver; Hauser, Hubert; Müller, Claas; Bläsi, Benedikt (2017-08-05). "Characterizing the degradation of PDMS stamps in nanoimprint lithography". Microelectronic Engineering. 180: 40–44. doi:10.1016/j.mee.2017.05.049.
- S.V. Sreenivasan; Ian McMackin; Frank Xu; David Wang; Nick Stacey; Doug Resnick (2005). "Enhanced nanoimprint process for advanced lithography applications". Semiconductor Fabtech (25th edition). Archived from the original on November 15, 2007.
- Ph.D Thesis "Development of Nanoimprint Lithography for Applications in Electronics, Photonics and Life-sciences" by Patrick Carlberg from Lund University, Sweden
- Goswami, Debkalpa; Munera, Juan C.; Pal, Aniket; Sadri, Behnam; Scarpetti, Caio Lui P. G.; Martinez, Ramses V. (2018-05-18). "Roll-to-Roll Nanoforming of Metals Using Laser-Induced Superplasticity". Nano Letters. 18 (6): 3616–3622. doi:10.1021/acs.nanolett.8b00714. ISSN 1530-6984. PMID 29775318.
- Cheng, X.; Jay Guo, L. (2004). "A combined-nanoimprint-and-photolithography patterning technique". Microelectronic Engineering. 71 (3–4): 277–282. doi:10.1016/j.mee.2004.01.041.
- S. Landis et al., Nanotechnology 17, 2701-2709 (2006).
- Li, M.; Chen, L.; Chou, S.Y. (May 2001). "Direct three-dimensional patterning using nanoimprint lithography". Applied Physics Letters. 78 (21): 3322–4. Bibcode:2001ApPhL..78.3322L. doi:10.1063/1.1375006.
- Calafiore, Giuseppe; Koshelev, Alexander; Allen, Frances I; Dhuey, Scott; Sassolini, Simone; Wong, Edward; Lum, Paul; Munechika, Keiko; Cabrini, Stefano (2016). "Nanoimprint of a 3D structure on an optical fiber for light wavefront manipulation". Nanotechnology. 27 (37): 375301. arXiv:1605.06415. Bibcode:2016Nanot..27K5301C. doi:10.1088/0957-4484/27/37/375301. PMID 27501300.
- Hsu, K.H.; Schultz, P.L.; Ferreira, P.M.; Fang, N.X. (2007). "Electrochemical Nanoimprinting with Solid-State Superionic Stamps". Nano Lett. 7 (2): 446–451. Bibcode:2007NanoL...7..446H. doi:10.1021/nl062766o. PMID 17256917.
- Chou, S.Y.; Keimel, C.; Gu, J. (2002). "Ultrafast and Direct Imprint of Nanostructures in Silicon". Nature. 417 (6891): 835–837. Bibcode:2002Natur.417..835C. doi:10.1038/nature00792. PMID 12075347.
- Massimo Tormen; Enrico Sovernigo; Alessandro Pozzato; Michele Pianigiani; Maurizio Tormen (2015). "Sub-100 μs nanoimprint lithography at wafer scale". Microelectronic Engineering. 141: 21–26. doi:10.1016/j.mee.2015.01.002.
- Shevchenko, E.V.; Talapin, D.V.; Kotov, N.A.; O’brien, S.; Murray, C.B. (2006). "Structural diversity in binary nanoparticle superlattices" (PDF). Nature. 439 (7072): 55–59. Bibcode:2006Natur.439...55S. doi:10.1038/nature04414. PMID 16397494.
- US 7128559
- M. LaPedus, "Toshiba claims to 'validate' nanoimprint litho," EETimes, October 16, 2007.