Calcination refers to heating a solid to high temperatures in absence of air or oxygen, generally for the purpose of removing impurities or volatile substances. However, calcination is also used to mean a thermal treatment process in the absence or limited supply of air or oxygen applied to ores and other solid materials to bring about a thermal decomposition. The root of the word calcination refers to its most prominent use, which is to remove carbon from limestone through combustion to yield calcium oxide (quicklime). This calcination reaction is CaCO3(s) → CaO(s) + CO2(g). Calcium oxide is a crucial ingredient in modern cement, and is also used as a chemical flux in smelting. Industrial calcination generally emits carbon dioxide (CO
2), making it a major contributor to climate change.
A calciner is a steel cylinder that rotates inside a heated furnace and performs indirect high-temperature processing (550–1150 °C, or 1000–2100 °F) within a controlled atmosphere.
The process of calcination derives its name from the Latin calcinare (to burn lime) due to its most common application, the decomposition of calcium carbonate (limestone) to calcium oxide (lime) and carbon dioxide, in order to create cement. The product of calcination is usually referred to in general as "calcine", regardless of the actual minerals undergoing thermal treatment. Calcination is carried out in furnaces or reactors (sometimes referred to as kilns or calciners) of various designs including shaft furnaces, rotary kilns, multiple hearth furnaces, and fluidized bed reactors.
Examples of calcination processes include the following:
- decomposition of carbonate ores, as in the calcination of limestone to drive off carbon dioxide;
- decomposition of hydrated minerals, as in the calcination of bauxite and gypsum, to remove water of crystallization as water vapor;
- decomposition of volatile matter contained in raw petroleum coke;
- heat treatment to effect phase transformations, as in conversion of anatase to rutile or devitrification of glass materials;
- removal of ammonium ions in the synthesis of zeolites;
- defluorination of uranyl fluoride to create uranium dioxide and hydrofluoric acid gas.
Calcination reactions usually take place at or above the thermal decomposition temperature (for decomposition and volatilization reactions) or the transition temperature (for phase transitions). This temperature is usually defined as the temperature at which the standard Gibbs free energy for a particular calcination reaction is equal to zero.
In limestone calcination, a decomposition process that occurs at 900 to 1050ºC, the chemical reaction is
- CaCO3(s) → CaO(s) + CO2(g)
Today, this reaction largely occurs in a cement kiln.
The standard Gibbs free energy of reaction is approximated as ΔG°r ≈ 177,100 − 158 T (J/mol). The standard free energy of reaction is 0 in this case when the temperature, T, is equal to 1121 K, or 848 °C.
In some cases, calcination of a metal results in oxidation of the metal to produce a metal oxide. In the seventeenth century, Jean Rey noted that lead and tin when calcinated gained weight, presumably as they were being oxidized.
Alchemists distinguished two kinds of calcination, actual and potential. Actual calcination is that brought about by actual fire, from wood, coals, or other fuel, raised to a certain temperature. Potential calcination is that brought about by potential fire, such as corrosive chemicals; for example, gold was calcined in a reverberatory furnace with mercury and sal ammoniac; silver with common salt and alkali salt; copper with salt and sulfur; iron with sal ammoniac and vinegar; tin with antimony; lead with sulfur; and mercury with aqua fortis.
There was also philosophical calcination, which was said to occur when horns, hooves, etc., were hung over boiling water, or other liquor, until they had lost their mucilage, and were easily reducible into powder.
- IUPAC. "Calcination".
- "High-Temperature Processing with Calciners".
- Mosby's Medical, Nursing and Allied Health Dictionary, Fourth Edition, Mosby-Year Book Inc., 1994, p. 243
- Gilchrist, J.D. (1989). Extraction Metallurgy (3rd ed.). Oxford: Pergamon Press. p. 145. ISBN 978-0-08-036612-8.
- This article incorporates text from a publication now in the public domain: Chambers, Ephraim, ed. (1728). "Calcination". Cyclopædia, or an Universal Dictionary of Arts and Sciences (1st ed.). James and John Knapton, et al.